220 mig would be the fastest and easiest IMO.. 110 migs work well on sheet metal and most will say they are fine on frames as well. Always use gas not a fan of flux core welding. If you have ass loads of time the tig would be awesome no clean up on welds ect. I usually only use my tig on parts that I can weld on the bench/exhaust.
|